Home Products High temperature repair agent

SD113 aluminum patching agent

Brand: SANDAO

MOQ: 10 Pieces

Delivery time: 15 Day

SD113 aluminum repair agent is a high performance polymeric metal material obtained from a variety of alloy materials and modified toughening heat resistant resin Material, with a very high strength, and excellent wear and corrosion resistance and aging resistance characteristics, good construction technology, curing without shrinkage; wear and corrosion resistance, aging resistance. The cured material has high strength and can be machined. With a high binding strength with the metal, the color can be maintained with the repaired substrate and can be processed together with the substrate.

Product Details

■Describe

◆Product model: SD113 aluminum repair agent

◆SD113 aluminum repair agent is a high performance polymeric metal material obtained from a variety of alloy materials and modified toughened heat resistant resin Material, has a high binding strength with metal, the color can be maintained with the repaired matrix and can be processed together with the substrate.

■Apply

It is suitable for the repair of gray iron, ball iron and other casting defects and the repair of parts wear, corrosion and rupture. After repair, the color is basically the same as the substrate, with high strength, and excellent wear and corrosion resistance and aging resistance, and can carry out all kinds of mechanical processing together with the substrate.

■Main technical indicators (AtTA = 25℃)

Operable time limit(min)	curing time	Curing time is required before full-load operation	working temperature(℃)	Maximum tolerance temperature(℃)
30～60	At 24h or 2h + 80℃ 1h	48h	-60～150	170

parameter	performance index
pigment	aluminium
aluminium	Paste
Density (g/cm3)	1.42
compression strength (Mpa)GB/T 1041-2008	955
shear strength(Mpa)GB/T 7124-2008	263
bending strength (Mpa)GB/T 9341-2008	334
tensile strength (Mpa)GB/T 6329-2009	515
hardness	86

■Use method and matters needing attention

1. Surface treatment: rough the repaired surface and clean it with cleaning agent.

2. Preparation: Mix A and B components A: B: 6:1 or volume ratio A: B: 4:1, and use them up within the specified operation time limit.

3. Apply: apply the mixed material layer by layer to the parts to be repaired. The first layer should be compacted to make it fully infiltrated with the substrate. If the order after the need for mechanical processing, to leave an appropriate amount of processing allowance.

4. Curing: 20~25℃ curing for 8 hours can be machining, 24 hours later into use, if the temperature is low should be used heating or extended curing time to promote curing.